    DD-P-6007/DD-I-2180
     
    鞋底原液 产品说明书
    The Product Description of shoes sole
    产品名称:DD-P-6007/DD-I-2180
    Name of product
    Q/G991002
    NO.014
    1. 特性: 高密度,高粘结性,耐低温
    Characteristics: high density, high adhesion, Low temperature resistant
    Usage: apply to the manufacture of In the labor insurance shoes outsole, bottom
    3. 原液特性:
    Characteristics:
    品   名
    Name of Products
    外   观
    Appearance
    粘   度
    Viscosity
    (mPa·s/40℃)
    密   度
    Density
    (g/cm3/40℃)
    包  装
    Package
    (kg)
    DD-P-6007
    液状或蜡状
    Liquid, or waxy
    1200~2400
    1.17~1.19
    18
    DD-I-2180
    透明液体无异物
    Transparent Liquid without objects
    200~500
    1.18~1.20
    20
    4. 催化剂与辅助剂:
    Catalyst and Adjuvant
         大底  DD-P-6007/DD-SM-2/水=18kg/350g/5g  中底  DD-P-6007/DD-SM-2/水=18kg/350g/50g
    Outsole                               insole
    5. 成型条件及物性值:
    Condition of molding and Physical Properties:
    反应性
    Reactivity
    技术参数
    Technical Parameters
    项  目
    Items
    参考物性值
    Reference Physical Properties
    大底
    Outsole
    中底
    insole
    大底
    Outsole
    中底
    insole
    参考配比
    Mix Ratio
    P+C/I 
    100/58~60
    100/60~62
    试片密度(g/cm3
    Sample Density
    0.50
     
    使用温度(℃)
    Temperature(℃)
    40~45/38~42
    40~45/38~42
    硬度(C型)
    Hardness
    70~75
    45~50
    乳白时间(s)
    Cream Time(s)
    6~8
    5~7
    拉伸强度(MPa)
    Tensile Strength
    6.0~8.0
    4.0~5.0
    升起时间(s)
    Rise Time(s)
    30~40
    30~35
    伸长率(%)
    Elongation
    500~600
    450~550
    自由泡密度
    Free Foam Density
    (g/cm3
    0.4~0.6
    0.25~0.32
    撕裂强度
    Tearing Strength
    (kN/m)
    60.0~80.0
    20.0~30.0
    金属模具温度
    Mold Temperature
    (℃)
    40~50
    40~50
    试片收缩率(%)
    Shrinkage
     
     
    脱模时间
    Demold Time
     
    (min)
    3~4
    3~4
    脆化温度
    Fragile Temperature
    (℃)
    -45~-35
     
    鞋底成型密度
    Molded Temperature of Sole
    (g/cm3
    0.7~1.0
    0.45~0.55
    耐折性(23℃)
    Flexins Resistance
    (裂口长度,mm)
    (Crack Length,mm)
    无裂痕
    Crackless
     
    成型鞋底硬度(C型)
    Molded Hardness of Sole
    70~75
    45~50
    NBS耐磨(%)
    NBS Abrasion Resistance
    (预除表皮后数据)
    (Data Free of Skin)
    ≥60
     
     
    ●配合比率是以最佳配比值为基础,此配比值会随添加的颜料助剂种类和添加量不同而变化。
    Mix Ratio is based on the best matching ratio, it varies with different added catalogue and volume of pigment assist.
    ●自由泡沫密度会依季节(温度,湿度)的不同而变化。
      Free Foam Density changes from season to season,especially the temperature and humidity.
    ●脱模时间会随成型品厚度的增加而延长。
    Demold Time extends with the increase of the thickness of moldings.
    ●该物性数据是对6 mm厚的试验片测试获得的数据
    The above-data of Physical Properties is based on the test of a 6mm-thick testing piece.
    ●耐折条件:屈挠角度为 90度,频率为100次/min*5万次。
    Condition of Flexins Resistance: curve angle is 90 degrees, and frequency is 100times/min*50000times
    ●      以上数据仅作参考,具体数据以实际操作为准。
    The above information is provided for ireference only, the specific data is subject to the practical operation.
     